- unique hybrid ceramic with a dual ceramic-polymer network structure
- available as mono- and multichromatic types in up to three translucency levels (T, HT, ST)
VITA ENAMIC®
A new definition of stability.
![](https://www.vita-zahnfabrik.com/portal/sap/medien/c/cc0/cc0c01/Buehne_ENAMIC.jpg)
- fabricating durable restorations using a high-load capacity hybrid ceramic with absorption of masticatory forces
- non-/minimally invasive restorations possible since the elastic hybrid ceramic enables reduced wall thicknesses
- fabricating accurate, precise and delicate restorations using a hybrid material with integrated elasticity
- cost-effective reconstruction, thanks to time-saving CAM fabrication and efficient polishing without any firing process
Recommended indications*
- reconstructions with reduced wall thicknesses that preserve natural tooth structure
- posterior crowns that offer high load capacity in cases with limited space availability
- precise repair of small defects (e.g., indirect cervical fillings/delicate inlays)
- non-/minimally-invasive reconstruction of occlusal surfaces (table top)
- monolithic veneering structures for digital hybrid bridges
*) These are recommended indications; the entire range of single tooth restorations can normally be fabricated. For details, please refer to the respective working instructions of the products.
- translucent (T)
VITA SYSTEM 3D MASTER®
0M1, 1M1, 1M2, 2M1, 2M2, 2M3, 3M1, 3M2, 3M3, 4M2 - high translucent (HT)
VITA SYSTEM 3D MASTER®
0M1, 1M1, 1M2, 2M1, 2M2, 2M3, 3M1, 3M2, 3M3, 4M2 - super translucent (ST)
VITA SYSTEM 3D MASTER®
1M1, 1M2, 2M2, 3M2, 4M2 - ENAMIC IS
VITA SYSTEM 3D MASTER®
1M1, 1M2, 2M2, 3M2, 4M2
Blocks (mm):
- translucent (T) / high translucent (HT) / super translucent (ST)
EM-14 (12 x 14 x 18) - high translucent (HT)
EM-10 (8 x 10 x 15) - ENAMIC IS
IS-14 (12 x 14 x 18 mm)
IS-16 (16 x 18 x 18 mm)
VITA ENAMIC® products
VITA ENAMIC® for CEREC®/inLab® VITA SYST
Description | Prod. no. 5 pcs. |
---|---|
0M1-HT, EM-10 |
EC40M1HTEM10 8 x 10 x 15 mm |
0M1-HT, EM-14 |
EC40M1HTEM14 12 x 14 x 18 mm |
0M1-T, EM-14 |
EC40M1TEM14 12 x 14 x 18 mm |
1M1-HT, EM-10 |
EC41M1HTEM10 8 x 10 x 15 mm |
1M1-HT, EM-14 |
EC41M1HTEM14 12 x 14 x 18 mm |
1M1-T, EM-14 |
EC41M1TEM14 12 x 14 x 18 mm |
1M2-HT, EM-10 |
EC41M2HTEM10 8 x 10 x 15 mm |
1M2-HT, EM-14 |
EC41M2HTEM14 12 x 14 x 18 mm |
1M2-T, EM-14 |
EC41M2TEM14 12 x 14 x 18 mm |
2M2-HT, EM-10 |
EC42M2HTEM10 8 x 10 x 15 mm |
2M2-HT, EM-14 |
EC42M2HTEM14 12 x 14 x 18 mm |
2M2-T, EM-14 |
EC42M2TEM14 12 x 14 x 18 mm |
3M2-HT, EM-10 |
EC43M2HTEM10 8 x 10 x 15 mm |
3M2-HT, EM-14 |
EC43M2HTEM14 12 x 14 x 18 mm |
3M2-T, EM-14 |
EC43M2TEM14 12 x 14 x 18 mm |
2M1-T, EM-14 |
EC4EM3112765 12 x 14 x 18 mm |
2M3-T, EM-14 |
EC4EM3132765 12 x 14 x 18 mm |
3M1-T, EM-14 |
EC4EM3192765 12 x 14 x 18 mm |
3M3-T, EM-14 |
EC4EM3212765 12 x 14 x 18 mm |
4M2-T, EM-14 |
EC4EM3282765 12 x 14 x 18 mm |
2M1-HT, EM-10 |
EC4EM4112645 8 x 10 x 15 mm |
2M1-HT, EM-14 |
EC4EM4112765 12 x 14 x 18 mm |
2M3-HT, EM-10 |
EC4EM4132645 8 x 10 x 15 mm |
2M3-HT, EM-14 |
EC4EM4132765 12 x 14 x 18 mm |
3M1-HT, EM-10 |
EC4EM4192645 8 x 10 x 15 mm |
3M1-HT, EM-14 |
EC4EM4192765 12 x 14 x 18 mm |
3M3-HT, EM-10 |
EC4EM4212645 8 x 10 x 15 mm |
3M3-HT, EM-14 |
EC4EM4212765 12 x 14 x 18 mm |
4M2-HT, EM-10 |
EC4EM4282645 8 x 10 x 15 mm |
4M2-HT, EM-14 |
EC4EM4282765 12 x 14 x 18 mm |
1M1-ST, EM-14 |
EC4EM7062765 12 x 14 x 18 mm |
1M2-ST, EM-14 |
EC4EM7072765 12 x 14 x 18 mm |
2M2-ST, EM-14 |
EC4EM7122765 12 x 14 x 18 mm |
3M2-ST, EM-14 |
EC4EM7202765 12 x 14 x 18 mm |
4M2-ST, EM-14 |
EC4EM7282765 12 x 14 x 18 mm |
VITA ENAMIC® UNIVERSAL VITA SYSTEM 3D-MA
Description | Prod. no. 5 pcs. |
---|---|
0M1-HT, EM-10 |
EN1EM4022645 8 x 10 x 15 mm |
0M1-HT, EM-14 |
EN1EM4022765 12 x 14 x 18 mm |
0M1-T, EM-14 |
EN1EM3022765 12 x 14 x 18 mm |
1M1-HT, EM-10 |
EN1EM4062645 8 x 10 x 15 mm |
1M1-HT, EM-14 |
EN1EM4062765 12 x 14 x 18 mm |
1M1-T, EM-14 |
EN1EM3062765 12 x 14 x 18 mm |
1M2-HT, EM-10 |
EN1EM4072645 8 x 10 x 15 mm |
1M2-HT, EM-14 |
EN1EM4072765 12 x 14 x 18 mm |
1M2-T, EM-14 |
EN1EM3072765 12 x 14 x 18 mm |
2M2-HT, EM-10 |
EN1EM4122645 8 x 10 x 15 mm |
2M2-HT, EM-14 |
EN1EM4122765 12 x 14 x 18 mm |
2M2-T, EM-14 |
EN1EM3122765 12 x 14 x 18 mm |
3M2-HT, EM-10 |
EN1EM4202645 8 x 10 x 15 mm |
3M2-HT, EM-14 |
EN1EM4202765 12 x 14 x 18 mm |
3M2-T, EM-14 |
EN1EM3202765 12 x 14 x 18 mm |
4M2-HT, EM-10 |
EN1EM4282645 8 x 10 x 15 mm |
4M2-HT, EM-14 |
EN1EM4282765 12 x 14 x 18 mm |
4M2-T, EM-14 |
EN1EM3282765 12 x 14 x 18 mm |
1M1-ST, EM-14 |
EN1EM7062765 12 x 14 x 18 mm |
1M2-ST, EM-14 |
EN1EM7072765 12 x 14 x 18 mm |
2M2-ST, EM-14 |
EN1EM7122765 12 x 14 x 18 mm |
3M2-ST, EM-14 |
EN1EM7202765 12 x 14 x 18 mm |
4M2-ST, EM-14 |
EN1EM7282765 12 x 14 x 18 mm |
VITA ENAMIC® IS for CEREC®/inLab® VITA S
Description | Prod. no. 5 pcs. |
---|---|
1M1-HT, IS-16L |
EC4EM4069485 18 x 16 x 18 mm |
1M1-HT, IS-16S |
EC4EM4069365 18 x 16 x 18 mm |
1M1-T, IS-14L |
EC4EM3069725 18 x 14 x 12 mm |
1M1-T, IS-14S |
EC4EM3069605 18 x 14 x 12 mm |
1M2-HT, IS-16L |
EC4EM4079485 18 x 16 x 18 mm |
1M2-HT, IS-16S |
EC4EM4079365 18 x 16 x 18 mm |
1M2-T, IS-14L |
EC4EM3079725 18 x 14 x 12 mm |
1M2-T, IS-14S |
EC4EM3079605 18 x 14 x 12 mm |
2M2-HT, IS-16L |
EC4EM4129485 18 x 16 x 18 mm |
2M2-HT, IS-16S |
EC4EM4129365 18 x 16 x 18 mm |
2M2-T, IS-14L |
EC4EM3129725 18 x 14 x 12 mm |
2M2-T, IS-14S |
EC4EM3129605 18 x 14 x 12 mm |
3M2-HT, IS-16L |
EC4EM4209485 18 x 16 x 18 mm |
3M2-HT, IS-16S |
EC4EM4209365 18 x 16 x 18 mm |
3M2-T, IS-14L |
EC4EM3209725 18 x 14 x 12 mm |
3M2-T, IS-14S |
EC4EM3209605 18 x 14 x 12 mm |
4M2-HT, IS-16L |
EC4EM4289485 18 x 16 x 18 mm |
4M2-HT, IS-16S |
EC4EM4289365 18 x 16 x 18 mm |
4M2-T, IS-14L |
EC4EM3289725 18 x 14 x 12 mm |
4M2-T, IS-14S |
EC4EM3289605 18 x 14 x 12 mm |
VITAVM®LC
Light-curing, microparticle composite for extraoral use with fixed and removable restorations
VITA AKZENT® LC
Reliable reproduction of individual shade effects
VITA ENAMIC® Polishing Set
For simple pre- and high-gloss polishing of VITA ENAMIC hybrid ceramic
VITA ADIVA® FULL-ADHESIVE
The full-adhesive luting system with perfectly matched components for conditioning tooth substance and restorative material
VITA ADIVA® SELF-ADHESIVE
The self-adhesive luting system with perfectly matched components for conditioning the restorative material
VITA ENAMIC – SYSTEM SOLUTIONS*
VITA offers VITA ENAMIC with specific holder systems for the CAD/CAM systems:
- CEREC/inLab (Dentsply Sirona)
- PlanMill 40/PlanMill 40S/PlanMill 50S (Planmeca)
- Ceramill mikro IC/Ceramill Motion 2/Ceramill Matik (Amann Girrbach AG)
VITA ENAMIC – UNIVERSAL SOLUTIONS*
- CORiTEC Serie (imes-icore GmbH)
- Röders RXD Serie(Röders GmbH)
- DGSHAPE DWX Serie (DGSHAPE Corporation)
- CS 3000/CS3100 (Carestream Dental, Inc)
- Zfx Inhouse5x (Zfx GmbH)
- Milling UNIT M Serie (Zirkonzahn S.r.l.)
- N4/R5/S1/S2/Z4 (vhf camfacture AG)
- Organical Desktop Serie (R+K CAD/CAM Technologie GmbH)
- DMG ULTRASONIC-Serie (DMG Mori AG)
*) Note: The range of VITA CAD/CAM material versions/geometries/shades available may vary for individual CAD/CAM system partners or systems. The hardware and software requirements in each case are available from the respective CAD/CAM system partners.
Easy download for multiple documents
Download a .zip file containing all the selected files in a single step.Simply tick the files then click here.
A dry treatment site must be provided for the adhesive bonding technique. Rubber dam and/or retraction cords are suitable for keeping the site dry. Please make sure that any excess bonding material is completely removed from the sulcus.
- Due to the industrial fabrication of VITA ENAMIC using a combination of hot curing and pressure application, all parameters are ideally arranged. As a result, with VITA ENAMIC (polymer part), a complete absence of residual monomers is guaranteed.
Conventional bonding using cements is contraindicated since sufficient load capacity and retention of the VITA ENAMIC crown on the abutment is only achieved by adhesive bonding.
....... and if so, how?
- You can perform surface characterization using the VITA ENAMIC Stains Kit. It is comprised of a shade powder and liquid, which you should apply to the surface after it has been conditioned and prior to light-curing. A light-curing glaze is then applied as a seal.
- As indicated in the working instructions, only diamond-coated milling tools should be used. We advise against using carbide milling tools for finishing. Due to the high proportion of ceramic-network content, this could lead to abrasion, and as a result, to black streaks or spots on your restoration. For polishing, we recommend the VITA ENAMIC Polishing Set instruments.
.... to repeat the application before continuing the work?
To ensure reliable bonding of abutment and crown, the abutment needs to be degreased with ethanol before further processing and the process step of "Priming" needs to be repeated.
- VITA ENAMIC Glaze is a light-curing resin. That is why you should ensure that no direct light sources are directed onto the object during application. You should also avoid brushing the same area several times with the brush. This can also result in streaks.
- Please check your light-curing device, as well as its
wavelength and compare these to the information in the working instructions. A sticky surface indicates that curing has not been fully completed. The surface
must be dry after curing, and no longer sticky. The surface is similar to that of a polished crown. Reworking is not required.
..... Glaze or polished to high gloss?
Subgingival portions of the crown should be polished since a high-gloss surface of a crown reduces plaque accumulation.
Temporary bonding of VITA ENAMIC crowns to abutments is not recommended since the required load capacity is only guaranteed after definitive and firm bonding of the VITA ENAMIC crown.
- HT (High Translucent) are used for inlays and onlays, all-ceramic and partial crowns, as well as for veneers. HT block materials offer a very beautiful chameleon effect. This makes them particularly suited to natural dentition when transferring the shade of the tooth stump. T (Translucent) are better for masking the underlying structure thanks to greater shade intensity, which is why we recommend it for discoloration and decalcification, as well as for older patients with a reduced proportion of enamel.
- The silicate ceramic network is ideally suited to etching and provides a highly retentive etching pattern for micro-mechanical bonding between the material and the luting composite. That is a significant difference between ENAMIC and composite materials.
.... (Al2O3) prior to bonding the crown? Is it also possible to sandblast with glass beads?
Defined surface enlargement and mechanical roughness are only achieved by sandblasting the abutment with Al2O3 prior to bonding the crown; in combination with the chemical compound (using a primer), reliable adhesive bonding of the crown to the abutment is achieved. Glass beads are not suitable for this purpose.
- In order to achieve effective bonding between the VITA ENAMIC surface and the characterization material or the luting composite, the surface of the VITA ENAMIC material must be conditioned. This is due to the high proportion of ceramic-network content. You have two possible approaches to choose from. You can either etch the material using a 5% hydrofluoric acid gel such as VITA CERAMIC ETCH, or you can sandblast it using AL2O3 of max. 50 µm at a pressure level of max. 1 bar.
.... for adhesive bonding of VITA ENAMIC crowns to zirconia abutments?
These monomers in the primer/bonding agent and/or bonding composite enable chemical bonding of the sandblasted zirconia surface and the bonding material.
- It creates an additional chemical bond between the
ceramic network and luting materials as well as VITA ENAMIC Stains.
.... and what needs to be done in cases of screw loosening after bonding of the crown?
In such cases, simple trepanning of VITA ENAMIC crowns with a suitable milling or grinding tools can be carried out. Then prepare the access to the screw channel of the abutment. Tighten the prosthetic screw to the prescribed torque. Then follow the recommendations to seal the screw channel. Use phosphoric acid gel (30 sec) to clean the opening in the crown and then apply an adhesive/silane bonding agent. Light-curing restorative composites with high opacity are suitable to seal the opening. Please observe the corresponding instructions for use.
- As a user, ideally you will need a CEREC/inLab MC XL milling system and the corresponding 3D software from Version > 4.0 to perform processing. It is important to note: VITA ENAMIC offers excellent milling properties – it can be processed more quickly, and at the same time, does not wear milling tools to the same extent.
- So that the material can also be milled with the small CEREC / inLab milling system and using software versions earlier than 4.0, please select VITABLOCS Mark II, I14.
.... walls caused by a titanium abutment?
In such cases, high-opacity bonding materials with masking capacity should be used. Translucent adhesive materials, which are used, e.g. for veneers, are less suitable.
- Adhesive bonding of VITA ENAMIC restorations must be performed using light-curing or dual-curing fine hybrid composites. A self-adhesive composite such as RelyX Unicem from 3M ESPE can also be used for bonding crowns (dentin adhesion). Adhesive bonding of crowns should preferably be performed using a flowable, dual-curing composite (depending on the thickness of the layering).
...... should be used?
- In order to achieve a natural surface shine, we recommend a two-step approach. The VITA ENAMIC Polishing Set provides special polishing instruments for this purpose. You should ensure that the specified rotational speed is observed in this case and work at a low level of contact pressure. These polishing tools have been specially designed for the new material, allowing you to achieve ideal results.
- For custom surface design, you can then use a goat hair brush and diamond polishing paste to achieve a surface shine tailored to your particular needs.
To seal the screw channel, first apply gutta-percha, Teflon tape, or a similar material into the screw channel; then apply a suitable bonding agent into the opening and seal it tightly using a light-curing restorative composite.
Clinical case. How Thin is Thin?
by CEREC Digest, Hsuan Chen
The story of our single-visit ultrathin veneer challenge. With VITA ENAMIC.
December 25, 2017 by Hsuan Chen
CEREC Digest was founded in 2016 by Hsuan Chen (陳鉉) and Cheng-Han Li (李承翰). The plan was to create a channel that focuses on the CEREC system and dental CAD/CAM in general. The website was launched in January of 2017 as a joint effort between CEREC Asia, a training center based in Taiwan, and the Tooth Faerie Club, a 50-person study club created by Hsuan and Cheng-Han. The Digest caters primarily to the demographic of dentists and dental technicians who are interested to learn more about digital dentistry.